RG1,5SA Self Adhesive

Transcription

1 Description of Product: Self adhesive membrane with a thickness of 1.5mm, consisting of rubberized bitumen with adhesive additives, glassfiber carrier, removable PP film at bottom and high density polyethylene film at top. Reinforcement: Glassfiber reinforcement gives Rumba excellent dimensional stability especially at hot weather conditions. Surface Finish: Siliconize Removable PP film at bottom and high density polyethylene film at top. Typical Application Areas: Applied on surfaces which are to be protected against water penetration: Roofs- protection of cement roofs, protection of wooden roofs, even with high sloping; protection of ventilated metal roofs. Concrete- Ideal for waterproofing concrete, masonry and wood surfaces where in-service temperatures will not exceed 54 C. Use with Bitumex Primers. Features and Benefits: Eliminated the need for torching or mopping Ensured quick, clean and easy lapping of rolls No open flame on your roof Clean and neat application Safe application 100% UV protected Basic Application Instructions: Applied Cold. Need primer application before membrane application. Surface Preparation and Priming: A fundamental requirement of any bituminous membrane system is that it must provide protection from all weather conditions likely to be experienced during its design life. All individual layers in a bituminous membrane system must be watertight, and together the whole system must be waterproof. Application area should be removed from stains and be smooth. For this purpose, Bitumen Primer needs to be applied on surface before application. Cover primed surfaces with self-adhered roofing membranes the same day.

2 Application of Membrane: Fully Adhered 1- Starting at the roof drains and vertical to the roof slope, apply the self-adhesive membrane without adhering in parallel lines. Unroll onto the below surface for alignment. Do not immediately remove the release sheet. 2. Overlap the membrane next to another along the side lap and the ends. Side overlap creates longitudinal overlap between two sheets. End overlap creates a join between shorter sides of the sheets To overlap at side laps, just remove the PP bant (7.5cm) and apply to the adjacent membrane pratically. Ensure full adherence. Stagger the end joints by a minimum of 61cm. 3.Release the PP film and adhere this part of the self-adhesive membrane to the surface. Relase PP film on the remaining part at a 45 angle to avoid wrinkles in the self-adhesive membrane sheet. 4. Overlap adjacent self-adhesive membrane by 9cm. Overlap end laps by 15cm. Stagger end laps by a minimum of 61cm. Finish with weighted roller to ensure a continuous adherence to the surface.

3 Safety Precaution: Bitumex products must be applied by qualified applicators who have received an adequate training, for the prevention and the protection (in particular for the use of the extinguishers) against accidents caused by the combustible or flammable materials, of liquefied propane gas, open flame and their material of installation. Check the construction and the composition of the systems of roof and the walls before applying. Ensure the cleanliness of the places. Use only proper torching equipment in perfect working order certified by local standard organizations. Use only proper hoses suited for propane gas of less than 15m. Verify and tighten all the connections before the use of the equipment. Do not light the torch if a propane odour is present. Never seek a leak with a flame. Use soapy water. Use a torch whose gas output is adjustable with a stopping device. Follow the specifications, notices and documentations of the manufacturer and site authorities. The wearing of gloves, long sleeves, long trousers, safety boots, helmet and safety glasses is recommended. Do not wear synthetic fabrics. Remove clothing contaminated with solvents. Avoid skin contact. Good working practices, high standarts of personal hygiene and plant cleanliness must be maintained at all times. Whilst using, do not eat, drink or smoke. In the event of any localised changes in appearance or texture of the skin being noticed, medical advice should be sought without delay. Contact with hot product will cause burns. Ensure good ventilation and avoid, as far as reasonably practicable, the inhalation and contact with vapours, mists or fumes which may be generated during use. If such vapour, mists or fumes are generated, their concentration in the workplace air should be controlled to the lowest reasonably practicable level. Avoid contact with eyes. Highly toxic hydrogen sulphide gas may be emitted from hot product and accumulate in enclosed spaces or tanks. Extreme care must therefore be taken during venting of closed spaces which have, at any time contained hot product. Under no circumstances should entry be made in to small enclosures without taking full precautions.

4 Storage: Flashings must be stored in such a way to prevent any creasing, twisting, scratches and other damages of the roof. The materials will be protected adequately and stored permanently away from flames or welding sparks, protected from bad weather and any harmful substances. Keep all membranes upright. 1. Rolls should always be stored and transported at upright position. 2. Membrane pallets should not be stored on top of each other and similarly, heavy loads should never be placed on membrane pallets. 3. Bituminous membranes should be stored at closed areas where room temperature is above +5C. They should never be stored outside as pallets are exposed to direct sun shine and should always be kept away from heat sources. 4. Membrane rolls should not be laid outside if there is no cover on them. High temperature may lead to longitudinal shrinkage and latitudinal expandage at membranes with polyester carrier. For bituminous membranes, recommended shelf-life is 12 months. Later than this date, membrane performance is diminishing. Packaging: Pallets are covered by UV Resistant White Shrinks Roll Size : 1mtx20mt 1,5mm Rolls per pallet: 25Rolls (By Container) and 30Rolls(By Truck)

5 Product Details Unit Tolerance RG1,5SA Modification of Bitumen Reinforcement Upper surface coating Lower surface coating TS EN Test Method Unit SBS Fibre Glass HDPE PP Removable Film Visual defects TS EN none Thickness TS EN mm ±0,2 1,5 Length TS EN m min(-0,03) 20 Width TS EN cm min(-2) 100 Straightness TS EN pass Watertightness (10kPa) TS EN kPa pass Reaction to Fire TS EN E class External Fire Performance ENV NPD Watertightness after stretching TS EN NPD Peel resistance of joints TS EN N/50mm ±30% 38 Water vapour properties TS EN 1931 min Tensile strength (MD/CMD) TS EN N/50mm 400/300 Elongation (MD/CD) TS EN % 2/2 Impact resistance TS EN 12691Mtd.A mm min 700 Tearing resistance (with nail) TS EN N/50mm ±20% 150 Dimensional Stability TS EN % max 0,6 Cold Bending TS EN 1109 C min -10 Flow Resistance TS EN 1110 C min 100 TS EN Impact resistance TS EN 12691Mtd.A min 700 Resistance to Chemicals Cold Bending TS EN 1109 C min -10 Tearing resistance (with nail) TS EN N/50mm ±20% 150 Sheer resistance of joints TS EN N/50mm ±20% 250 Water vapour properties TS EN 1931 min Resistance to static loading TS EN Mtd.B Kg min 5 Tensile strength (MD/CMD) TS EN N/50mm 400/300 Elongation (MD/CD) TS EN % 2/2 Reaction to Fire EN NPD Dangerous Substances none none NPD

6