Technical. Data Sheet. 3M Scotchlite Reflective Material 5535 Segmented Flame Resistant Trim. October Description. Retroreflective Performance

Transcription

1 Technical Data Sheet October M Scotchlite Reflective Material 5535 Segmented Flame Resistant Trim Description 3M Scotchlite Reflective Material 5535 Segmented Flame Resistant Trim is designed for use on safety garments requiring flame resistance as defined, for example, in test methods ASTM F1506 or ISO When properly used, 3M Scotchlite Reflective Material 5535 Segmented Flame Resistant Trim helps to enhance the visibility of the wearer in night-time or low-light conditions when illuminated by a light source such as vehicle headlights, by returning the light back toward the original source and reaching the driver s eye. 3M Scotchlite Reflective Material 5535 Segmented Flame Resistant Trim is composed of wide angle, exposed retroreflective lenses bonded to a heat activated adhesive. The trim is 50.8mm (2 inches) wide and comprised of reflective patterned segments on a blue plastic liner. Retroreflective Performance The coefficient of retroreflection (R A, in cd/lux/m²) is measured by methods traceable to either of the following retroreflective intensity testing procedures: ASTM E and E (R A ) CIE 54.2:2001 (R ) Reflected colour of 3M Scotchlite Reflective Material 5535 Segmented Flame Resistant Trim is white. The R A values were measured at the listed specific entrance and observation angles. Representative retroreflective performance data were generated by 3M and are based on testing new product. Use, wear, laundering, and environmental conditions will affect performance. Please contact your 3M representative for proposed product specifications. Product Certification EN ISO 20471, ANSI/ISEA 107 and CAN/CSA Z96 3M Scotchlite Reflective Material 5535 Segmented Flame Resistant Trim is certified to the current versions of EN ISO High Visibility Clothing Test Methods and Requirements and ANSI/ISEA 107 American National Standard for High-Visibility Safety Apparel and Headwear for Level 2 retroreflective performance. It will meet the requirements for the current version of CAN/CSA Z96 High Visibility Safety Apparel.

2 3M Scotchlite Reflective Material Product Number Daytime Colour Initial Average R A 1 Minimum R A 2 Wash Cycles Segmented Flame Resistant Trim Silver > Measured by 3M on new product at +5.0 entrance and 0.2 observation angles 2 EN ISO and ANSI/ISEA 107 minimum coefficient of retroreflection for Level 2 retroreflective material at +5 entrance angle and 0.2 observation angle 3 ISO 6330 Method 6N and Method 2A at 60 C (140 F) and R A 100 cd/lux/m 2 3M Scotchlite Reflective Material 5535 Segmented Flame Resistant Trim is not certified for marine safety applications requiring IMO type approval. 3M Scotchlite Reflective Material SOLAS Grade Products have this type of certificate. Fire-fighter and Flame Retardant Standards Approvals 3M Scotchlite Reflective Material 5535 Segmented Flame Resistant Trim is certified to the current edition of various standards as components for fire fighting and technical rescue clothing and equipment, when applied to compliant fabrics such as certain aramids, modacrylics, and FR treated cottons. These standards include current editions of: NFPA 1971 Standard on Protective Clothing and Equipment for Structural Fire Fighting and Proximity Fire Fighting; NFPA 1977 Standard on Protective Clothing and Equipment for Wildland Fire Fighting; NFPA 1951 Standard on Protective Ensembles for Technical Rescue Incidents; NFPA 2112: Standard on Flame-Resistant Garments for Protection of Industrial Personnel Against Flash Fire; CAN/CGSB Fireline Workwear for Forest Firefighters, or CAN/CGSB Firefighters Protective Clothing for Protection Against Heat and Flame; CGSB Workwear for Protection Against Hydrocarbon Flash Fire; EN 469 : 2005 Protective Clothing for Fire-fighters - Performance Requirements for Protective Clothing for Firefighting; EN ISO : 2008 Protective Clothing - Protection Against Heat and Flame - Limited Flame Spread Materials, Material Assemblies and Clothing; ISO : Protective Clothing for Use in Welding and Allied Processes; and ISO : 2008 Protective Clothing - Clothing to Protect Against Heat and Flame. Performance While the use of 3M Scotchlite Reflective Material enhances visibility, no reflective material can guarantee absolute visibility, particularly in adverse weather conditions or unusually harsh wear conditions. Performance will vary depending upon actual use, exposure conditions, and proper cleaning/maintenance. Users should test reflective material to satisfy conformance to their own requirements. 3M recommends that all customers, in accordance with good manufacturing practices, establish an ongoing quality management system. The quality management system should include, on an ongoing basis, monitoring of the finished garment that helps to ensure compliance to the stated claims. Please visit our website, Scotchlite.com for new or updated technical literature or contact your local 3M Technical Service Representative. Physical Performance 3M Scotchlite Reflective Material 5535 Segmented Flame Resistant Trim will meet or exceed the following physical performance as noted. All R A values are at +5 entrance angle and 0.2 observation angle. See the current product certificates available from your local 3M sales or technical service representative for test laboratory and test date - note that different laboratories may be used for different certificates.

3 Physical Performance 3M Scotchlite Reflective Material Segmented Flame Resistant Trim Test Methods, Certifications Retroreflectivity: Initial ANSI/ISEA Level 2 (Table 4); CAN/CSA Z96-02 Level 2 ; EN ISO 20471:2013, 6.1 Abrasion: R A 100 Flexing: R A 100 Cold Fold: R A 100 Temperature Cycle: R A 100 Wash: R A 100 EN 530 Method 2 and ISO , 5000 cycles ISO 7854 Method A, 7500 cycles ISO 4675, -20 C (-4 F) C (122 F), C (-22 F) ISO 6330 Method 2A and Method 6N, C (140 F) Wet Reflectivity: R A 100 ANSI/ISEA , Appendix A; ISO 20471, Annex C; current editions of: NFPA 1971; NFPA 1977; NFPA 1951 Flame Resistance 4 ASTM D6413, 4 char length, 2 seconds after flame; ISO 11611:2007, 6.7; ISO 11612:2008, 6.3; ISO 14116:2008, 6.1; EN 469:2005,B3.2; current editions of: NFPA 1971; NFPA 1977; NFPA 1951; NFPA 2112; CGSB 155.1; CGSB ; CGSB Heat Resistance 4 ISO 17493, C (500 F); ISO 11612:2008, 6.2; EN 469:2005, B3.1; current editions of: NFPA 1971; NFPA 1977; NFPA 1951; NFPA 2112; CGSB 155.1; CGSB ; CGSB Convective Heat C (285 F), current editions of: NFPA 1971; NFPA 1977; NFPA 1951; NFPA 2112; CGSB 155.1; CGSB ; CGSB ; No convective heat test in Europe Arc Thermal Performance Value 4 : ATPV 5 cal/cm 2 Application Instructions ASTM F1959 Whenever two or more pieces of 3M Scotchlite Reflective Material are used together on a single surface or as a set, they should be matched to ensure uniform colour and reflectivity. All safety garments should be constructed in accordance with the appropriate standards. Cutting: Hand-cut or guillotine Heat Lamination Work on a flat surface where uniform heat and pressure can be applied. Avoid applying film over seams and stitches. Place transfer film on fabric substrate with the adhesive side down and apply heat and pressure as described in table below. Use a non-stick slip sheet to protect the reflective surface. The lamination temperature, time and pressure listed below should be used as a guide. Each substrate and reflective film combination should be tested to determine the best set of conditions that will meet customer requirements. Other lamination methods, such as roll to roll, heat fusing and HF welding can also be used. The proper temperature, time and pressure conditions must be tested for each fabric to ensure adequate adhesion and physical performance. 3M Scotchlite Reflective Material Product Number Temperature Dwell Time Line Pressure 5535 Segmented Flame Resistant Trim C ( F) 20 seconds Firm (30-40 psi) Note - The optimal application temperature and pressure will vary depending on substrate and equipment. Manufacturers should carry out tests to determine appropriate conditions for each and every application.

4 Handling Precautions This product contains an aluminium layer as part of the construction. Blemishing of this aluminium layer can occur if the front surface of the product has direct contact from hands during application and is then exposed to hot and humid conditions greater than 27 C (80 F) and greater than 70% relative humidity for a period of weeks. These blemishes do not affect performance of the product. Please refer to 3M Technical Bulletin Care Guidelines to Reduce Staining on 3M Scotchlite Reflective Material. Care and Maintenance Instructions Important: Test each application according to appropriate care instructions required for the finished product. Actual life of 3M Scotchlite Reflective Material 5535 Segmented Flame Resistant Trim depends on cleaning methods and wear conditions. Care label recommendations: Caution Washing/cleaning conditions harsher than those recommended below could diminish the brilliance of the fabric and shorten the product s lifetime significantly. The following instructions therefore must be strictly followed. No pre-soaking. No application of high alkaline products (e.g. heavy duty products or stain removal products). No application of solvenated detergents or micro-emulsions. No additional bleaches. Do not overdry. Before use, the suitability of the intended care process for 3M Scotchlite Reflective Material Segmented Flame Resistant Trim must be determined. Test duration should mirror the anticipated maximum number of care cycles in use. Homewash Washing Conditions A coloured clothing wash programme without pre-wash should be used. Recommendation: Wash temperature: Max. wash time at highest wash temperature: Max. programme time: Recommended load ratio Detergent: 30 C to 60 C 12 minutes 60 minutes 70% Brand powdered household detergents should be used. Recommended are detergents for delicate or coloured laundry. Refer to the detergent manufacturer s recommendations for dosage in areas of high water hardness and for various degrees of garment soiling.

5 The use of bleach or detergents containing organic solvent will result in a reduction in retroreflective performance. Use of temperatures lower than 40 C will increase the lifetime of the reflective fabric. Actual lifetime will be dependent upon the detergent system and its dosage level. Do not bleach Do not pre-soak laundry even in a low concentration of bleach. Drying Conditions Tumble Dry: Tumble drying should be performed in a commercially available household dryer using the medium dry setting. Exhaust temperature should not exceed 50 C. Do not overdry. Damp dry only. Air Drying: Line drying is recommended where possible. Commercial Wash Washing Conditions The washing machine should be a front-loading, open pocket washer extractor. Tunnel washing is not recommended. The wash process should be based on a one-bath (main-wash) or a two-bath process (pre- and main-wash) followed by a cool down, if needed, and three rinse cycles. Extended rinsing is recommended to completely remove all detergent residues. Load factor should not exceed 70 %, with the liquor ratio for washing in the range of 1:4 to 1:5 and for rinsing in the range of 1:6 to 1:8. Wash temperature should not exceed 75 C. Total time of the pre- and main- wash bath should not exceed 20 minutes. Detergent: Low-to-medium alkaline, high-surfactant detergents are preferred. The detergent should not contain free sodium hydroxide or potassium hydroxide. For specific information on recommended detergents contact your 3M representative. Controlled detergent dosage should give actual wash lye concentration not exceeding those detailed below: Parameter Recommended Maximum ph-value 10.5 to 11.0 < 11.6 Active Alkalinity Na 2 O sodium oxide < 650 mg/l < 1000 mg/l (Alkalinity titration against phenolphthalein endpoint, without BaCl 2 addition).

6 Note: The wash load should have a ph value in the range of 5.5 to 6.5 after the final rinse. Detergent systems with a high alkaline strength, containing organic solvents or free sodium / potassium hydroxide should not be used. Detergent systems and sour shall not contain any oxidising chemicals e.g. chlorine bleach. Use of a lower ph and lower active alkalinity may increase the lifetime of the reflective fabric. Actual lifetime will depend upon the actual wear & care impact. No chlorine bleach Do not pre-soak laundry even in a low concentration of bleach. Drying Conditions Tumble Dry: Load ratio: 1:25. The drying process must be controlled to ensure that the exhaust temperature does not exceed 90 C. The drying process should be continued until the load is damp dry. Maximum drying time should not exceed 20 minutes. Tunnel finish: Inlet temperature should not exceed 160 C. Depending on the fabric the drying time should be about 7 minutes. Do not overdry. Fabric temperature should not exceed 135 C at any time during drying. Spray steam pressure should not exceed 4 bar. The distance between the garments during the finishing process should be in a range of mm. Dry Cleaning Dry Cleaning Conditions Dry Cleaning is not recommended. Ironing Ironing Conditions Use low setting. Use press cloth. Do not apply steam.

7 Product Availability 3M Scotchlite Reflective Material 5535 Segmented Flame Resistant Trim is available in rolls with the following standard width and lengths although some roll dimensions may not be available in every country or region. 3M Scotchlite Reflective Material Product Number Roll Width Width Tolerance Standard Roll Length 5535 Segmented Flame Resistant Trim 50.8 mm (2 in.) ±0.5 mm (±0.02 in.) Storage and Shelf Life 100 m (109 yd) 200 m (218 yd) In order to preserve performance, store in a cool, dry area and use within one year after date of receipt. Store rolls in original shipping cartons. Return partially used rolls to the carton or suspend horizontally through the core. Cut pieces should be stored flat. Important Notice to Purchaser / Converter / Wearer: All statements, technical information and recommendations herein are based on tests we believe to be reliable, but the accuracy or completeness thereof is not guaranteed. We shall not be liable and no warranty shall apply for products not applied according to our published information folder. Before using/converting, the user/converter must determine the suitability of the product for its intended use/converting, and the user/converter assumes all risk and liability whatsoever in connection therewith. All questions of warranty and liability relating to this product are governed by the terms of the sale subject where applicable to the prevailing law. No statement or recommendation not contained herein shall have any force or effect unless in an agreement signed by officers of us. Personal Safety Division EMEA Region 3M Centre, Cain Road, Bracknell Berkshire RG12 8HT United Kingdom Tel: +44 (0) M and Scotchlite are trademarks of 3M. Please recycle. 3M All rights reserved. DS EU_Master_01